Single Side Red Thickness 12um Copper Foil Rolls
Quickly details
. Low profile and Single side side treatment in red.
. Thickness: 12um
. Width: ≤520 mm
. Length: ≤5000 M
. ID: 76 mm,152 mm
. Alloy: C11000
Features:
1. Red color
2. Good performance in resistant to bending suitable for FCCL.
3. High density performance leads to high flexibility
Application:
Suitable for FCCL, FPC, COVERLAY, BONDING FILM
TDS for FPC FCCL with all thickness.
| Thickness | 0.10/0.012/0.018/0.025/0.035mm | Width | ≤520mm | ||||
| Item | Unit |
Parameter | |||||
| Thickness | MM | 0.010 | 0.012 | 0.018 | 0.025 | 0.035 | |
| Grade | － | C1100 | C1100 | C1100 | C1100 | C1100 | |
|
Copper content | % | ≥99.95 | ≥99.95 | ≥99.95 | ≥99.95 | ≥99.95 | |
| Area Weight | g/m2 | 89±3 | 107±4 | 160±5 | 222±7 | 305±10 | |
| Roughness | (RA) | Um | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
| (RZ) | Um | ≤1.7 | ≤1.7 | ≤1.7 | ≤1.7 | ≤1.7 | |
|
Tensile Strength(MP) | State normal | Mpa | ≥360 | ≥380 | ≥400 | ≥400 | ≥400 |
| State temper (180℃) | Mpa | ≥160 | ≥160 | ≥160 | ≥160 | ≥160 | |
|
Elongation(%) | State normal | % | ≥1.0 | ≥1.2 | ≥1.4 | ≥1.4 | ≥1.4 |
| state temper l(180℃) | % | ≥7 | ≥8 | ≥10 | ≥10 | ≥10 | |
| MIT | State normal | Time | ≥2400 | ≥2400 | ≥2400 | ≥2400 | ≥2400 |
| state temper (180℃) | Time | ≥2400 | ≥2400 | ≥2400 | ≥2400 | ≥2400 | |
| Peel strength | N/mm | ≥0.8 | ≥1.0 | ≥1.3 | ≥1.35 | ≥1.4 | |
| High temperature oxidation resistance(180℃ 1hour) | － | Qualified
| Qualified
| Qualified
| Qualified
| Qualified
| |
Remark:
Common Width: 520(±1)mm,according to the customer request.
FAQ:
Q1: Can you supply the sample?
A: We can supply A4 samples and rolls sample ,but need take some cost.
Q2. Do you test all your goods before delivery?
A: Yes, we have, we can provide TDS before delicery.
Q3. what is your standard width?
A: 520mm and 620mm,we accept customization for the width. we can cut it into any size that you demand after pass discussing.